Epoxy finish product for general use in industry. Can also be applied to industrial floors, with special resistance to trampling. Applicable directly on iron, aluminum, galvanized iron and light alloys, limited to applications for internal use.
Water-based epoxy or acrylic primers.
Water-based paint products, because of their very low organic solvent content, are characterized by poor substrate wettability, which is much less than that of conventional solvent-based products. Therefore, the presence on the substrate of substances, such as grease, oil, grease and dirt (and of course, for other reasons, rust and calamine) is not tolerated. Cleanliness of the substrate is a necessary and fundamental condition so that the outcome of the painting is successful. Iron: SA2 grade sandblasting. Alternatively perfect mechanical cleaning of the substrate by sanding with removal of rust, calamine and subsequent cleaning by degreasing with aqueous solutions or solvents. Galvanized sheet: Thorough buffing or sanding, followed by degreasing with solvents. Aluminum: Mechanical cleaning by sanding, followed by degreasing with solvents. Concrete Floors: On concrete, remove dust and any traces of oil or grease. Concrete surfaces built at least four weeks ago: Always check residual moisture content (? 3% by weight) before painting. Moisture could also rise from the base by capillarity. Perform, the "plastic sheet test" (2m x 2m polyethylene sheet taped to the concrete surface to be painted). The sheet must remain in place for at least 24 hours, so any rising vapor that would condense on the sheet can be detected. In the case of particularly smooth surfaces (resulting from finishing treatments, for example, with a concrete helicopter), it is recommended to roughen (with processes such as grinding, sanding, sandpapering, etc.) and eliminate any kind of contamination (fats, oils, acids, cracks, cavities, etc.) that may preclude or affect paint adhesion.
Comp. A: KW112 + Water-based Tinters – PW 100 parts by weight Comp. B: CZW140 50 parts by weight Before mixing Component A and Component B, it is recommended to mix them well individually and then thoroughly mix the two components together. For applications on concrete, proceed with the first coat well thinned so that it penetrates well into the pores of the concrete. After 3 to 4 hours maximum proceed with the second, thicker coat to cover.
Epoxy finish WB
Semigloss
On request
1,35 Kg/l (± 0,05)
Thixotropic SOLID % - VOLUME (A+B) 38% (± 2) SOLID % - WEIGHT (A+B) 53% (± 2)