490.R7001 - SINTOFLEX INDUSTRIALE GRIGIO R.7001

FIELD OF APPLICATION:

Primer suitable for light carpentry work and various types of metal products

RECOMMENDED FINISHES:

One-component synthetic finishes, fast-drying synthetic, nitro.

PREPARATION OF THE SUBSTRATE:

Iron surfaces: SA2 sandblasting, or thorough mechanical cleaning followed by degreasing with solvents.

PREPARATION OF THE PRODUCT:

Comp. A: 490.R7001 100 parts by weight Thinner (*): D.434 20 - 30 parts by weight (*) Mix thoroughly until the color and consistency are uniform, then dilute to the desired viscosity with our D.434.

PRODUCT SPECIFICATIONS:

TYPE OF PRODUCT

Synthetic Industrial primer 1K

APPEARANCE

Matt

COLOUR

Grey – RAL 7001

SPECIFIC WEIGHT

1,50 Kg/l (± 0,05)

SUPPLY VISCOSITY

15” (± 3) DIN 8 at 25 °C SOLID % - VOLUME 56% (± 2) SOLID % - WEIGHT 73% (± 2)

DRYING TIME AT 20 °C.

Dry dust-free - Print-free: 4-5 hours. 10’ - 15’ - Print-free 1 - 2 hours   - Drying 24 - 36 hours   - Forced Drying 60’ - 70’ at 60 °C - 80 °C

RECOMMENDED LAYERS

1 (cross layers)

RECOMMENDED - DFT

40 - 50 µm (*)

THEORETICAL YIELD

10,9 m2/Lt or 7,3 m2/Kg at 50 µm dry (*) At greater thicknesses there may be problems with deep curing and/or removal during over-application.

APPLICATION INSTRUCTIONS:

View pictograms Page 1.

RECOATING:

After 4 hours minimum

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

The storage room must be dry and with a temperature between +10 °C and +35 °C. Rev.: 01/24 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.