994.90100 - MONOFLEX NERO - PRIMER ALTA ADESIONE

NATURE OF PRODUCT:

Very fast-drying single-component anticorrosive primer based on vinyl and epoxy resins with excellent adhesion qualities.

FIELD OF APPLICATION:

General purpose anchor primer: carpentry, metal furniture, fixtures, etc. Excellent direct adhesion on: Iron, Galvanized Iron, Aluminum.

PREPARATION OF THE SUBSTRATE:

Iron surfaces: Remove all traces of rust, grease and moisture by thorough mechanical cleaning, followed by degreasing with solvents. Aluminum: Carry out sanding treatment, degrease with solvents and then paint immediately. Galvanized sheet: Sand or pad and degrease with solvent.

PREPARATION OF THE PRODUCT:

Comp. A: 994.90100 100 parts by weight Diluent: D.525 / D.535 80 - 100 parts by weight Up to 5% retardant 10063P can be added, if needed.

PRODUCT SPECIFICATIONS:

TYPE OF PRODUCT

Single-component.

APPEARANCE OF THE FILM

Matte

COLORS

Black

SPECIFIC WEIGHT

0,97 Kg/l (± 0,05)

SUPPLY VISCOSITY

11”±2 DIN 8 at 25 °C

DRY RESIDUE

35% (±2)

DRYING AT 20 °C.

Dry dust-free - Print-free: 4-5 hours. 5’ – 10’   Drying 20’ – 30’ at 20 °C   Forced Drying 10’ – 15’ at 60 °C

RECOMMENDED LAYERS

A cross coat

RECOMMENDED THICKNESS

20 micron

THEORETICAL YIELD

14 m2/Lt-Kg at 20 micron

RECOATING:

Wet-on-wet after 20 to 60 minutes at 20 °C with fast-drying enamels, polyurethane epoxies and 2K acrylics. Overcoating with nitro enamels, nitrosynthetics and base coat is not recommended.

SAFETY REGULATIONS:

Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

In unopened and sealed packages, kept at a temperature of +5 to +30 °C. Rev.: 03/22 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.