KW162 - EPOLAK SEMILUC. BUCCIATO ALL''ACQUA

FIELD OF APPLICATION:

Epoxy finish for general use in industry, machine tools, industrial plants and carpentry. Applicable directly on iron, aluminum and galvanized sheet, limited to applications for internal use.

RECOMMENDED PRIMER:

Water-based epoxy primers.

PREPARATION OF THE SUBSTRATE:

Water-based paint products, because of their very low organic solvent content, are characterized by poor substrate wettability, which is much less than that of conventional solvent-based products. Therefore, the presence on the substrate of substances, such as grease, oil, grease and dirt (and of course, for other reasons, rust and calamine) is not tolerated. Cleanliness of the substrate is a necessary and fundamental condition so that the outcome of the painting is successful. Iron: SA2 grade sandblasting. Alternatively perfect mechanical cleaning of the substrate by sanding with removal of rust, calamine and subsequent cleaning by degreasing with aqueous solutions or solvents. Galvanized sheet: Thorough buffing or sanding, followed by degreasing with solvents. Aluminum: Mechanical cleaning by sanding, followed by degreasing with solvents.

PREPARATION OF THE PRODUCT:

Comp. A: KW162 + Water-based Tinters – PW 100 parts by weight Comp. B: CZW140 50 parts by weight Before mixing Component A and Component B, it is recommended to mix them well individually and then thoroughly mix the two components together. The dilution is a function of the final degree of peel you want to achieve and especially the application system. To find the best level of dilution, we recommend preliminary tests.

PRODUCT SPECIFICATIONS:

TYPE OF PRODUCT

Epoxy embossed finish WB

APPEARANCE

Half-glossy

COLOUR

On request

SPECIFIC WEIGHT (Comp.A)

1,35 Kg/l (± 0,05)

SUPPLY VISCOSITY

Thixotropic product SOLID % - VOLUME (A+B) 38% (± 2) SOLID % - WEIGHT (A+B) 53% (± 2)

DRYING TIME AT 20°C

Dry dust-free - Print-free: 4-5 hours. 30’   Touch-free 6 - 7 hours   Complete curing 24 - 48 hours   Forced Drying 60’ at 60 °C   Maximum chemical resistance after 10 days

RECOMMENDED LAYERS

1 (cross layers) Two coats if applied directly.

RECOMMENDED - DFT

60 - 70 µm

THEORETICAL YIELD (1)

6,3 m2/Lt or 4,8 m2/Kg at 60 µm dry

POT-LIFE AT 20 °C

90’. The pot-life decreases at higher temperatures. Under no circumstances should you apply product that has exceeded pot-life limits, as films would not ensure sufficient adhesion and chemical resistance. (1) In 75/25 ratio with PW900.

APPLICATION INSTRUCTIONS:

View pictograms Page 1.

RECOATING:

After complete drying of the product, minimum after 10 hours and within 36 hours. After 48 hours, light sanding of the film is recommended to ensure good adhesion of the top coat. Special peel airbrushes are recommended for application.

SAFETY REGULATIONS:

Water-based products must be protected from frost. Strictly follow the instructions on the labeling and in the safety data sheet.

STORAGE CONDITIONS:

Water-based products should be protected from frost, so the storage room should be dry and between +10 °C and +30 °C. Rev.: 01/24 The data and information contained in this sheet are the result of our experience and accurate laboratory tests. However, since the painting process represents a set of operations that are beyond our control, they do not therefore guarantee, in any way, the final performance of the cycle.

The data and information contained in this sheet are the result of our experience and accurate tests and laboratory tests.
However, since the painting process is a set of operations that are beyond our control, they therefore do not constitute, in any way any form of guarantee on the final performance of the cycle itself.